H10MnSi AWS EM13K Submerged Arc Welding Wire 2.5mm 25kg
Contact Person : Kevin Yin
WhatsApp : +8613812837333
| Minimum Order Quantity : | one pallet | Price : | USD 1 |
|---|---|---|---|
| Packaging Details : | Neutral box/ LT color box/OEM brand box | Delivery Time : | 15 WORKING DAYS |
| Supply Ability : | 1,200,000 TON PER YEAR |
| Place of Origin: | CHINA | Brand Name: | LONGTENG |
|---|---|---|---|
| Certification: | TUV CE, ABS, DB, ISO9001 | Model Number: | LT·H08MnA |
|
Detail Information |
|||
| Product Name: | Submerged Arc Welding Wire LT·H08MnA | Model: | LT·H08MnA |
|---|---|---|---|
| Brand: | LONGTENG | Diameter: | 2.5/3.2/4.0/5.0mm |
| Weight: | 25/50/250kg | Surface: | Cooper Plating |
| OEM: | Accept | ||
| High Light: | AWS Em12 Submerged Arc Welding Wire 4mm,H08MnA Submerged Arc Welding Wire 250kg,aws a5.17 em12 |
||
Product Description
LT·H08MnA 2.5/3.2/4.0/5.0mm Submerged Arc Welding Wire
LT·H08MnA Conform to Standard :GB/T 5293 H08MnA
AWS Em12
ISO 14171-B-SU22
Specification:It is a kind of medium manganese-low silicon type welding wire,matches with medium-manganese and medium-silicon welding flux,Insensitive to rust on the base metal, It has excellent bead molding and slag detach ability.The wire can be applied single or dual feeding with AC/DC.
Purpose:Using with sintered flux LT•SJ101 , it can be applied both for high-speed welding steel plate of tensile strength 420N/mm2 and filling welding
Chemical Composition(%)
| Chemical Composition | C | Mn | Si | S | P | Cr | Ni | Cu |
| Guarantee Value | ≤0.10 |
0.80~ 1.10 |
≤0.07 | ≤0.030 | ≤0.030 | ≤0.20 | ≤0.30 | ≤0.35 |
| General Result | 0.066 | 0.96 | 0.038 | 0.007 | 0.010 | 0.027 | 0.011 | 0.110 |
Mechanical Properties of Deposited Metal
|
Test item
Flux |
Rm(MPa) | ReL/Rp0.2(MPa) | A(%) |
KV2(J) -20℃ |
| LT•SJ101 | 415~550 | ≥330 | ≥22 | ≥27 |
Size of Welding Wires
| Size(mm) | Φ2.5 | Φ3.2 | Φ4.0 | Φ5.0 |
Notes:
1. Shielding gas: Adopt pure Argon gas. Recommendation flow rate: 9-14L/min (AMP 100-200A), 14-18L/min (AMP 200-300A).
2. Tungsten extension: 3-5mm, Arc length: 1-3mm.
3. Wind speed limited: ≤1.0m/s.
Argon gas shielding on back side of welding part will get better welding result.
4. Mechanic property and metal anti-cracking ability of the welded metal relative by energy pass value on the wire.
5. The welding should be operated in clean surface without rust, moist, oil contamination and dust.The above suggestions are for reference purpose. Evaluate and determine the situation of the scene before starting the wielding process.