H10Mn2 Aws A5.17 Eh14 Submerged Arc Saw Welding Wire 2.5mm 3.2mm 4.0mm 5.0mm

Minimum Order Quantity : one pallet Price : USD 1
Packaging Details : Neutral box/ LT color box/OEM brand box Delivery Time : 15 WORKING DAYS
Supply Ability : 1,200,000 TON PER YEAR
Place of Origin: CHINA Brand Name: LONGTENG
Certification: TUV CE, ABS, DB, ISO9001 Model Number: LT·H10Mn2

Detail Information

Product Name: Submerged Arc Welding Wire LT·H10Mn2 Model: LT·H10Mn2
Brand: LONGTENG Diameter: 2.5/3.2/4.0/5.0mm
Weight: 25/50/250kg Surface: Cooper Plating
OEM: Accept
High Light:

Aws A5.17 Eh14 Submerged Arc Saw Welding Wire

,

H10Mn2 submerged arc welding saw wire 2.5mm

,

AWS EH14 SAW Wire

Product Description

LT·H10Mn2 2.5/3.2/4.0/5.0mm Submerged Arc Welding Wire

 

AWS A5.17 EH14 Submerged arc welding wire is a copper coated steel wire, and it can be used in automatic submerged arc welding with welding flux. The weld metal has excellent mechanical properties.

 

LT·H10Mn2 Conform to Standard :GB/T 5293 H10Mn2

AWS EH14

ISO 14171-B-SU33

 

Specification: It is a kind of high-manganese type welding wire. It matches with low-manganese and low-silicon type welding flux. Insensitive to the rust on the base metal. It has excellent bead molding and slag detach ability. The wire can be applied single or dual feeding with AC/DC.

 

Purpose:Using with sintered flux LT•SJ101, it can be applied both for high-speed welding steel plate of tensile strength 490N/mm2 and filling welding.Mechanical properties of deposited metal is very stable.

 

Chemical Composition(%)

Chemical Composition C Mn Si S P Cr Ni Cu
Guarantee Value ≤0.12

1.50~

1.90

≤0.070 ≤0.035 ≤0.035 ≤0.20 ≤0.30 ≤0.35
General Result 0.066 1.62 0.011 0.011 0.011 0.013 0.007 0.12
 

Mechanical Properties of Deposited Metal

Test item

 

Flux

Rm(MPa) ReL/Rp0.2(MPa) A(%)

KV2(J)

 

-20℃ -40℃

LT•SJ101 490~650 ≥400 ≥22 ≥27
 

Size of Welding Wires

Size(mm) Φ2.5 Φ3.2 Φ4.0 Φ5.0

 

Notes:

1. The welding line energy will directly affect the mechanical properties of the weld metal. Before using it, users should make process assessments according to the welding conditions and develop appropriate technical specifications.
2. Do remove the rust, oil, water and other impurities on weldment before welding.