ER90S-G Welding Wire High Toughness Low-Alloy Steel
Contact Person : Kevin Yin
WhatsApp : +8613812837333
| Minimum Order Quantity : | one pallet | Price : | USD 1 |
|---|---|---|---|
| Packaging Details : | Neutral box/ LT color box/OEM brand box | Delivery Time : | 15 WORKING DAYS |
| Supply Ability : | 1,200,000 TON PER YEAR |
| Place of Origin: | CHINA | Brand Name: | LONGTENG |
|---|---|---|---|
| Certification: | TUV CE, ABS, DB, ISO9001 | Model Number: | GMAW SV08G2S (AWS A5.18 ER70S-6) |
|
Detail Information |
|||
| Product Name: | CO2 Gas Shielded Welding Wire ER70S-6 | Model: | GMAW SV08G2S |
|---|---|---|---|
| Brand: | LONGTENG | Diameter: | 0.8/0.9/1.0/1.2/1.6mm |
| Weight: | 1/5/15/20kg | Surface: | Cooper Plating |
| Spool Material: | Black Plastic Spool | Packing: | Color Box |
| OEM: | Accept | Diameter Of Spool: | 100/200/270/300mm |
| High Light: | CO2 Gas Shielded MAG Welding Wire,Copper Coated Mig Welding Wire,1.6mm Mig Welding Wire |
||
Product Description
CO2 Copper Coated Mig Welding Wire 1.6mm 1.2mm 1.0mm GMAW SV08G2S
GMAW LT*SV08G2S 0.8/1.0/1.2/1.6mm Cooper Coating Welding Wire
GMAW LT·SV08G2S Conform to Standard :
GB/T 8110 ER50-6
ISO 14341-A-G424C13Si1
AWS A5.18 ER70S-6
JIS YGW12
GMAW SV08G2S is a mild steel welding wire that contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. The high silicon content increases the fluidity of the weld pool, thus creating a smoother bead appearance and resulting in minimal post-weld grinding. This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO 2 and/or CO 2 mix
Purpose:
1. Used for welding all kinds of 500MPa structural steel parts.
2. Used for welding all kinds of 500MPa plates and pipes
Chemical Composition(%)
| Chemical Composition | C | Mn | Si | S | P | Ni | Cr | Mo | V | Cu |
| Guarantee Value | 0.06~0.15 | 1.40~1.85 | 0.80~1.15 | ≤0.025 | ≤0.025 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.03 | ≤0.50 |
| General Result | 0.077 | 1.45 | 0.87 | 0.013 | 0.012 | 0.017 | 0.031 | 0.002 | 0.004 | 0.125 |
Mechanical Properties of Deposited Metal
| Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) |
| -40℃ | ||||
| Guarantee Value | ≥500 | ≥420 | ≥22 | ≥47 |
| General Result | 555 | 450 | 29 | 77/95/83 |
| Size(mm) | Current range (A) | GAS flow rate(L/min) |
| Φ0.8 | 50~100 | 15 |
| Φ1.0 | 50~220 | 15~20 |
| Φ1.2 | 80~350 | 15~25 |
| Φ1.6 | 170~550 | 20~25 |