ER55-G .030 .035 Solid Welding Wire With Co2 Argon 0.8mm 1.0mm

Minimum Order Quantity : one pallet Price : USD 1
Packaging Details : Neutral box/ LT color box/OEM brand box Delivery Time : 15 WORKING DAYS
Supply Ability : 1,200,000 TON PER YEAR
Place of Origin: CHINA Brand Name: LONGTENG
Certification: TUV CE, ABS, DB, ISO9001 Model Number: LT·TH550-NQ-II

Detail Information

Product Name: Weathering Steel Solid Welding Wire LT·TH550-NQ-II Model: LT·TH550-NQ-II (ER55-G)
Brand: LONGTENG Diameter: 0.8/0.9/1.0/1.2/1.6mm
Weight: 1/5/15/20kg Surface: Cooper Plating
Spool Material: Black Plastic Spool Packing: Color Box
OEM: Accept Diameter Of Spool: 100/200/270/300mm
High Light:

ER55-G Solid Welding Wire

,

Co2 Argon Solid Welding Wire

,

ER55-G MAG Welding Wire

Product Description

ER55-G .030 .035 Solid Welding Wire With Co2 Argon 0.8mm 1.0mm

 

LT·TH550-NQ-II 0.8/1.0/1.2/1.6mm Weathering Steel Solid Welding Wire

LT·TH550-NQ-II Conform to Standard :TB/T 2374 ER55-G

GB ER55-1

 

Specification:It comes with Argon - rich gases protection. The deposited metal has good atmospheric corrosion resistance, crack resistance, good shaping and toughness.

 

Purpose:Suitable for welding 550MPa high strength weathering steel,such as construction machinery, bridges, etc.

 

Chemical Composition(%)

Chemical Composition C Mn Si S P Ni Cr Cu
Guarantee Value ≤0.10 1.20~ ≤0.60 ≤0.020 ≤0.025 0.20~ 0.30~ 0.20~
1.6 0.6 0.9 0.5
General Result 0.057 1.4 0.46 0.008 0.016 0.33 0.48 0.3

 

Mechanical Properties of Deposited Metal(Ar+20%CO2)
Test Item Rm(MPa) ReL/Rp0.2(MPa) A(%) KV2(J)
-40℃
Guarantee Value ≥550 ≥450 ≥22 ≥60
General Result 590 495 28 112/120/118
 
Reference Current(DC+)
Size(mm) Current range (A) GAS flow rate(L/min)
Φ0.8 50~100 15
Φ1.0 50~220 15~20
Φ1.2 80~350 15~25
Φ1.6 170~550 20~25

 

Notes on usage:
1.E.S.O. (Electrode Stick Out) must be kept between 15-25mm.
2.Proper welding conditions must be adopted according to the purpose as the bead appearance and penetration are both varied widely.
3. Use 100% Co2 or Ar + Co2 gas mixture as shielding gas.
4. Control within the optimal range of welding conditions for this wire as possible.