2.5mm 2mm Stainless Steel Welding Rod E308/308l-16 A102

Minimum Order Quantity : one pallet Price : USD 1
Packaging Details : Neutral box/ LT color box/OEM brand box Delivery Time : 15 WORKING DAYS
Supply Ability : 1,200,000 TON PER YEAR
Place of Origin: CHINA Brand Name: LONGTENG
Certification: TUV CE, ABS, DB, ISO9001,CCS Model Number: LT·A102

Detail Information

Product Name: Stainless Steel Electrodes LT·A102 Model: LT·A102
Brand: LONGTENG Diameter: 2.0/2.5/3.2/4.0/5.0
Weight: 5kg Type Of Coating: Calcium-Titanium
Packing: Plastic Box OEM: Accept
High Light:

2mm Stainless Steel Welding Rod

,

AWS E308-16 Stainless Steel Welding Rod

,

2.5mm Stainless Steel Welding Rod

Product Description

2.5 2mm Stainless Steel Welding Rod E308/308l-16 A102

 

LT·A102 2.0/2.5/3.2/4.0/5.0 mm Stainless Steel Electrodes

 

Weldcote Metals E308-16 electrodes are used to weld unstabilized 18-8 stainless steels such as Types 301, 302, 304, 305, and 308. Weldcote Metals E308-16 electrodes provide corrosion resistance and physical properties equal to or greater than the steels for which they are recommended.

 

Conform to Standard

GB/T 983 E308-16

AWS A5.4 E308-16

ISO 3581-A-E(19 9) R 3 2

ISO 3581-B-ES 308-16

 

Specification:A102 is a kind of Titanium calcium type coating Cr19Ni10 stainless steel electrode. The deposited metal has good mechanical properties and inter granular corrosion resistance. It has good welding performance and porosity resistance. Heat resistance coating and crack resistance. AC/DC both can be applied.

 

Chemical Composition(%)

Chemical Composition C Mn Si S P Cr Ni Mo Cu
Guarantee Value

0.08

0.50~

2.50

1.00

≤0.030 ≤0.040

18.0~

21.0

9.0~

11.0

0.75

0.75

General Result 0.041 1.35 0.69 0.008 0.022 19.5 9.6 0.064 0.10

 

 

Mechanical Properties of Deposited Metal

 

Test Item Rm(MPa) A(%)
Guarantee Value ≥550 ≥30

Reference Current(AC,DC+)
Diameter(mm) Φ2.0 Φ2.5 Φ3.2 Φ4.0 Φ5.0
Amperage(A) 40~80 50~100 70~130 100~160 140~200

 

 

Notes:

1. The electrode must be preheated at the temperature of 300°C for 1 hour. Preheat the rod whenever it is used

2. Preferred DC power supply, electric current should not be high.