ER90S-G Welding Wire High Toughness Low-Alloy Steel
Contact Person : Kevin Yin
WhatsApp : +8613812837333
| Minimum Order Quantity : | one pallet | Price : | USD 1 |
|---|---|---|---|
| Packaging Details : | Neutral box/ LT color box/OEM brand box | Delivery Time : | 15 WORKING DAYS |
| Supply Ability : | 1,200,000 TON PER YEAR |
| Place of Origin: | CHINA | Brand Name: | LONGTENG |
|---|---|---|---|
| Certification: | TUV CE, ABS, DB, ISO9001 | Model Number: | LT·ER70-G |
|
Detail Information |
|||
| Product Name: | High Strength Steel Solid Welding Wire LT·ER70-G | Model: | LT·ER70-G (ER100S-G) |
|---|---|---|---|
| Brand: | LONGTENG | Diameter: | 0.8/0.9/1.0/1.2/1.6mm |
| Weight: | 1/5/15/20kg | Surface: | Cooper Plating |
| Spool Material: | Black Plastic Spool | Packing: | Color Box |
| OEM: | Accept | Diameter Of Spool: | 100/200/270/300mm |
| High Light: | C02 Mig Mag Soldering Wire,0.8mm MAG Welding Wire,Copper Coated MAG Welding Wire |
||
Product Description
C02 Mig Mag Soldering Wire 0.8mm 15Kg Plastic Metal Spool Copper Coated Welding Wire SG2 ER70s-6
Features:
ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
Application:
Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Chemical Composition(%)
| Chemical Composition | C | Mn | Si | S | P | Ni | Mo | Ti | Cr | Cu |
| Guarantee Value | ≤0.11 | 1.40~ | ≤0.80 | ≤0.025 | ≤0.025 | 0.50~ | 0.20~ | ≤0.16 | ≤0.30 | ≤0.50 |
| 1.9 | 1.55 | 0.6 |
| Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) |
| -20℃ | ||||
| Guarantee Value | ≥670 | ≥610 | ≥16 | ≥27 |
| General Result | 740 | 645 | 23 | 121/128/126 |
Notes:
1. The welding electrodes should be preheated 2 hour at 300~350℃ before welding.
2. The impurities such as rust, oil stains and moisture must be cleared off of the work piece.